A study of the deformation and fracture of single-crystal gold films of high strength inside an electron microscope

Source abstract

Abstract Single-crystal films of gold in (111) orientation, and 500 to 2000 Å in thickness, have been prepared by an evaporation technique. A device has been constructed to allow these films to be strained in a controlled manner while under observation inside the electron microscope (Siemens Elmiskop I). It is shown, by the absence of observable plastic deformation, that the films deform elastically up to abnormally high strain values. This is confirmed, in the case of 500 Å films, by precision electron diffraction measurements, which indicate elastic strains as high as 1 to 1·5%. This represents a tensile strength several times that of hard-drawn gold wire. The high tensile strength occurs despite the presence of a high density of dislocations. Failure occurs once the elastic limit is exceeded. Detailed examination of the fractured specimens reveals that highly localized plastic deformation occurs immediately before fracture. The nature of the fracture process has been deduced from the micrographs, and it is shown that the catastrophic failure occurs as a result of the high stress level which exists when plastic deformation occurs, coupled with the stress concentrations which occur as localized thinning takes place.